Role of oxide dispersion in fatigue behaviour of ODS type steels

Public support

  • Provider

    Czech Science Foundation

  • Programme

    Standard projects

  • Call for proposals

    Standardní projekty 12 (SGA02009GA-ST)

  • Main participants

  • Contest type

    VS - Public tender

  • Contract ID

    106-09-1954

Alternative language

  • Project name in Czech

    Role oxidické disperze při únavovém chování ODS ocelí

  • Annotation in Czech

    Projekt je zaměřen na objasnění role jemné oxidické disperze jako zpevňujícího prvku během cyklické plastické deformace ODS ocelí. Je známo, že ODS feritické a feriticko/martensitické oceli mají delší životnost a výrazně vyšší odolnost proti cyklické degradaci zejména za zvýšených teplot ve srovnání se slitinami bez rozptýlené oxidické fáze. Za účelem zjištění odezvy zkoumaných materiálu na mechanické zatěžování budou na miniaturizovaných únavových vzorcích budou měřeny křivky životnosti, křivky zpevnění a cyklická deformační křivka od pokojové teploty do 800°C. TEM analýza bude sloužit ke studiu interakcí dislokace ? oxidická disperze a ke zkoumání mikrostruktury vzniklé během cyklického zatěžování. Vliv malých rozměrů vzorků na rychlost šíření únavových trhlin bude studován jednak experimentálně, měřením rychlostí šíření trhlin na plochých vzorcích s různou tloušťkou, jednak matematickým modelováním pomocí metody konečných prvků. Výsledky projektu by měly přispět k návrhu optimální struktury ODS oceli odpovídající nejlépe specifickým požadavkům projektu řízené jaderné fúze.

Scientific branches

  • R&D category

    ZV - Basic research

  • CEP classification - main branch

    JG - Metallurgy, metal materials

  • CEP - secondary branch

    BM - Solid-state physics and magnetism

  • CEP - another secondary branch

    JL - Fatigue and fracture mechanics

  • OECD FORD - equivalent branches <br>(according to the <a href="http://www.vyzkum.cz/storage/att/E6EF7938F0E854BAE520AC119FB22E8D/Prevodnik_oboru_Frascati.pdf">converter</a>)

    10302 - Condensed matter physics (including formerly solid state physics, supercond.)<br>20306 - Audio engineering, reliability analysis<br>20501 - Materials engineering

Completed project evaluation

  • Provider evaluation

    V - Vynikající výsledky projektu (s mezinárodním významem atd.)

  • Project results evaluation

    It was obtained a new information about fatigue behaviour of 3 different ODS steels in temperature range from 25 to 800°C and degradation mechanisms were described. Publishing activity was on high level (5 Jimp, 9 Jneimp and 4 contributions on conferences). Obtained results will be used as input for the next research activity in this branch. No problems were found. Final evaluation - excellent

Solution timeline

  • Realization period - beginning

    Jan 1, 2009

  • Realization period - end

    Dec 31, 2012

  • Project status

    U - Finished project

  • Latest support payment

    Apr 1, 2012

Data delivery to CEP

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

  • Data delivery code

    CEP13-GA0-GA-U/02:3

  • Data delivery date

    May 17, 2016

Finance

  • Total approved costs

    4,333 thou. CZK

  • Public financial support

    4,333 thou. CZK

  • Other public sources

    0 thou. CZK

  • Non public and foreign sources

    0 thou. CZK