EFFECT OF CARBON ADDITION ON PHASE COMPOSITION AND HIGH TEMPERATURE STRENGTH OF FE(3)AL-TYPE IRON ALUMINIDE WITH ZR

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F10%3A10108827" target="_blank" >RIV/00216208:11320/10:10108827 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
EFFECT OF CARBON ADDITION ON PHASE COMPOSITION AND HIGH TEMPERATURE STRENGTH OF FE(3)AL-TYPE IRON ALUMINIDE WITH ZR
Original language description
Iron aluminides of Fe(3)Al type with Zr addition are studied as good high-temperature resistant materials for structural applications. Generally, Zr addition leads to formation of Laves phase in the structure of ternary alloys. Presence of these phases enhances high-temperature mechanical properties. The effect of carbon addition on the phase composition of these ternary alloys was studied. Two ordered alloys with the similar Fe, Al and Zr content and different carbon content were compared. The phase composition was studied by light optical microscopy (LOM), scanning electron microscopy (SEM) with energy dispersive analysis (EDA) and X-ray diffraction analysis (XRD). High-temperature mechanical properties are tested in tension.
Czech name
—
Czech description
—

Project
—
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2010
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)