Oriented SrFe(12)O(19) thin films prepared by chemical solution deposition

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F11%3A10103772" target="_blank" >RIV/00216208:11320/11:10103772 - isvavai.cz</a>
Alternative codes found
RIV/68378271:_____/11:00365562 RIV/61388980:_____/11:00365562
Result on the web
<a href="http://www.sciencedirect.com/science/article/pii/S0022459611005172" target="_blank" >http://www.sciencedirect.com/science/article/pii/S0022459611005172</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jssc.2011.09.024" target="_blank" >10.1016/j.jssc.2011.09.024</a>

Result language
angličtina
Original language name
Oriented SrFe(12)O(19) thin films prepared by chemical solution deposition
Original language description
Thin films of SrFe(12)O(19) (SrM) were prepared from a solution of iron and strontium alkoxides through the chemical solution deposition method on both amorphous (glassy SiO(2)), and single crystal substrates (Si(100), Si(111). Ag(111), Al(2)O(3)(001), MgO(111), MgAl(2)O(4)(111), SrTiO(3)(111)) substrates. The process of crystallization was investigated by means of powder diffraction, atomic force microscopy and scanning electron microscopy. Magnetization measurements, ferromagnetic and nuclear magneticresonance were used for evaluation of anisotropy in the films. Whilst amorphous substrates enabled growth of randomly oriented SrM phase, use of single crystal substrates resulted in samples with different degree of oriented growth. The most pronouncedoriented growth was observed on SrTiO(3)(111). A detailed inspection revealed that growth of SrM phase starts through the breakup of initially continuous film into isolated grains with expressive shape anisotropy and hexagonal habit. A co
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—

Project
<a href="/en/project/IAA100100803" target="_blank" >IAA100100803: Magnetoelectric ferrites</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)