Study of decomposition and stabilization of splat-cooled cubic gamma-phase U-Mo alloys
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F13%3A10143981" target="_blank" >RIV/00216208:11320/13:10143981 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.1016/j.jallcom.2013.04.168" target="_blank" >http://dx.doi.org/10.1016/j.jallcom.2013.04.168</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jallcom.2013.04.168" target="_blank" >10.1016/j.jallcom.2013.04.168</a>
Alternative languages
Result language
angličtina
Original language name
Study of decomposition and stabilization of splat-cooled cubic gamma-phase U-Mo alloys
Original language description
U-Mo alloys were prepared by splat cooling technique and characterized by X-ray diffraction. The alloys with 11-12 at.% Mo show a stable gamma degrees-phase, while those with 13-17 at.% Mo exhibit a pure gamma-phase at room temperature. All the splats become superconducting with T-c in the range from 1.24 K (pure U splat) to 2.11 K (U-15 at.% Mo). The phase transformation and stabilization of gamma-uranium phase in U-Mo alloys upon aging, annealing at 500 degrees C and 800 degrees C for time varying between 1 h and 144 h are described. Annealing at 500 degrees C leads to a decomposition of the gamma-phase, while annealing at 800 degrees C has stabilized the initial gamma-phase in U-Mo splat-cooled alloys. The gamma-phase U-15 at.% Mo alloy is stable tohydrogen exposure at atmospheric pressure (1 bar) and at room temperature; it does not absorb any detectable amount of hydrogen. Exposed to high pressure (80 bar) of H-2 gas it becomes hydride-powder (UH3Mo0.18) consisted of elongated pa
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Others
Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Journal of Alloys and Compounds
ISSN
0925-8388
e-ISSN
—
Volume of the periodical
580
Issue of the periodical within the volume
Neuveden
Country of publishing house
CH - SWITZERLAND
Number of pages
9
Pages from-to
223-231
UT code for WoS article
000324525800037
EID of the result in the Scopus database
—