Precipitation Effects in Cast, Heat-Treated and Cold-Rolled Aluminium AA7075 Alloy with Sc,Zr-Addition
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F21%3A10438906" target="_blank" >RIV/00216208:11320/21:10438906 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.4028/www.scientific.net/DDF.413.217" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/DDF.413.217</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/DDF.413.217" target="_blank" >10.4028/www.scientific.net/DDF.413.217</a>
Alternative languages
Result language
angličtina
Original language name
Precipitation Effects in Cast, Heat-Treated and Cold-Rolled Aluminium AA7075 Alloy with Sc,Zr-Addition
Original language description
The aluminium 7xxx series (Al-Zn-Mg-Cu-based) alloys are widely used in metalworking, transport industries as well as in space applications. The precipitation of the Al3(Sc,Zr) phase is known for its positive effect on a number of important utility properties, e.g. mechanical properties, recrystallization, temperature stability etc. Precipitation processes in the cast, cold-rolled and heat-treated aluminium 7xxx series materials with and without addition of Sc an Zr were investigated. Eutectic phase at grain boundaries with Zn, Mg and Cu content by microstructure observations was proved. Dissolution of the Zn, Mg (and Cu) containing (co-)clusters and Guinier-Preston (GP) zones and subsequent precipitation of the metastable phases from the Al-Zn-Mg-Cu system result the significant changes in hardening as well as in thermal response of the studied materials. Due to the presence of the high content of dislocations in materials after cold deformation and associated easier movement of atoms (Zn, Mg (and Cu)) the precipitation effects are shifted to lower temperature intervals compared to materials without rolling. Hardening values of the materials after high temperature heat treatment increase immediately from the beginning of natural ageing thanks to the irregular Zn, Mg (and Cu) containing formations, very probably (co-)clusters, GP zones and their precursors. Sc and Zr elements added to the aluminium 7xxx series alloy caused a higher microhardness values after annealing above ~ 270 °C. The nanosized Al3(Sc,Zr) phase has only a small influence on the development of the (co-)clusters, GP zones and their precursors. Coincidence Doppler broadening of the positron annihilation investigations confirmed that the early precipitation stages consist of Mg and Zn (and Cu) elements. Concentration of the last named element (Cu) in the early precipitation stages is likely to increase with increasing natural annealing length. Results of positron lifetime measurements of the cast as well as heat-treated materials after natural ageing showed that the thermal vacancy component is not negligible.
Czech name
—
Czech description
—
Classification
Type
C - Chapter in a specialist book
CEP classification
—
OECD FORD branch
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2021
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Book/collection name
Advances in Mass and Thermal Transport in Engineering Materials II
ISBN
978-3-0357-2771-5
Number of pages of the result
8
Pages from-to
217-224
Number of pages of the book
228
Publisher name
Trans Tech Publications Ltd
Place of publication
Baech
UT code for WoS chapter
—