Phase equilibria in the Ni-Al-Cr-Co system
Original language description
The Ni-Al-Cr-Co system was studied in the region of appearance of disordered gamma and ordered gamma' phase. Positions of phase boundaries and chemical composition of gamma and gamma' phases were calculated using software package ThermoCalc. A few experimental alloys were prepared and consequentially annealed to reach an equilibrium state. After annealing compositions of experimentally found phases were obtained by means of X-ray analysis in scanning transmission electron microscope. Results obtained from calculations were compared with experimental data and necessity of modification of thermodynamic parameters was found to reach better agreement between calculations and experiments.
Czech name
Fázové rovnováhy v systému Ni-Al-Cr-Co
Czech description
Systém Ni-Al-Cr-Co byl experimentálně zkoumán při teplotách 1273 a 1373 K a byla získána nová experimentální data v oblastech výskytu fází gamma, gamma', alfa a beta. Tyto experimentální údaje byly následně srovnány s teoretickými výpočty a byla nalezenanutnost změny některých termodynamických parametrů. Pro lepší porozumění chování systému Ni-Al-Cr-Co je potřeba provést další experimentální pozorování.