Nanocrystalline alpha-Fe Layer Examined by Mossbauer Spectrometry

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F14%3A00076363" target="_blank" >RIV/00216224:14310/14:00076363 - isvavai.cz</a>
Alternative codes found
RIV/68081723:_____/14:00431841 RIV/68081731:_____/14:00431841 RIV/68081723:_____/14:00531547 RIV/68081731:_____/14:00531547
Result on the web
<a href="http://przyrbwn.icm.edu.pl/APP/apphome.html" target="_blank" >http://przyrbwn.icm.edu.pl/APP/apphome.html</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.12693/APhysPolA.126.94" target="_blank" >10.12693/APhysPolA.126.94</a>

Result language
angličtina
Original language name
Nanocrystalline alpha-Fe Layer Examined by Mossbauer Spectrometry
Original language description
A few micrometers thick nanocrystalline alpha-Fe layer with the mean crystallite size d(X RD) = 14 nm was deposited in low-pressure microwave plasma, using Fe(CO)(5) vapour. Its nanocrystalline character was proved on its surface under SEM (surface was formed of deposited nanoparticles) and in its volume using TEM (deposited nanoparticles were stacked up, creating columns). No significant iron oxide phases were observed in the transmission Fe-57 Mossbauer spectrum measured at 5 K nor in the surface-sensitive Fe-57 conversion electron Mossbauer spectrum measured at 293 K.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BL - Plasma physics and discharge through gases
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)