The Non-Isothermal Kinetics of Sb2S3 In (GeS2)0.2(Sb2S3)0.8 Glass
Original language description
The crystallization of Sb2S3 in the (GeS2)0.2(Sb2S3)0.8 glass was studied under non-isothermal conditions. The influence of the sample form on crystallization was studied using bulk sample and two fractions of powder sample. The crystallization process of the sample in the form of powder was described using autocatalytic model, the crystallization of the bulk sample was described using nucleation-growth model. The parameters of both the models were determined.
Czech name
Kinetika neizotermní krystalizace Sb2S3 ve skle (GeS2)0.2(Sb2S3)0.8
Czech description
Byla studována neizotermní krystalizace Sb2S3 ve skle (GeS2)0.2(Sb2S3)0.8. Vliv charakteru vzorku na průběh krystalizace byl sledován pomocí objemového vzorku a dvou frakcí vzorku ve formě prášku. Průběh krystalizace vzorku ve formě prášku byl popsán pomocí autokatalytického modelu, krystalizace objemového vzorku byla popsána nukleačně-růstovým modelem. Byly určeny parametry obou modelů.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
CF - Physical chemistry and theoretical chemistry
OECD FORD branch
—

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)