Properties of alkali-activated aliminosilicate composite after thermal treatment

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F05%3APU53519" target="_blank" >RIV/00216305:26110/05:PU53519 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Properties of alkali-activated aliminosilicate composite after thermal treatment
Original language description
The investigation of the properties of alkali-activated aluminosilicate composite after exposure to high temperatures is reported in the present paper. The specimens were composed of finely ground blast furnace slag and dried sodium silicate as an activator. The heat-resistant mixture of vermiculite and electrical porcelain in volume ratio 30/70 was used as an aggregate. The specimens were tested after exposure to temperatures from 100 to 1200 C and microstructure, porosity and 28-days flexural and comppressive strengths were obtained.
Czech name
Vlastnosti alkalicky aktivovaných aluminosilikátových kompozitů po tepelném namáhání
Czech description
Tento článek prezentuje studium vlastností alkalicky aktivovaných aluminosilikátových kompozitů po tepelném namáhání. Vzorky byly připraveny z jemně mleté vysokopecní strusky a sušeného křemičitanu sodného jako aktivátoru. Jako kamenivo byla použita žáruvzdorná směs vermikulitu a elektroporcelánu v poměru 30/70. Připravené vzorky byly vystaveny teplotám 100 až 1200 C a poté byly zkoumány jejich vlastnosti.

Project
<a href="/en/project/GA103%2F04%2F0139" target="_blank" >GA103/04/0139: Analysis of properties of alkali-activated aluminosilicate materials exposed to high temperatures</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)