CORROSION RESISTIVITY OF CONCRETE WITH HIGHER CONTENT OF METAKAOLIN

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F09%3APU84863" target="_blank" >RIV/00216305:26110/09:PU84863 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

čeština

Original language name

Korozní odolnost betonů s vyšším obsahem metakaolínu

Original language description

Metakaolin may replace a part of Portland cement in concrete. The properties of concrete with metakaolin immersed 60 and 180 days in corrosion environments, such as chlorides, sulphates, magnesium and ammonium ions were investigated. The compressive strengths of specimens after corrosion loading were compared to the strengths of those cured in the drinking water at the same age. The results of determination of corrosion resistivity kKO present good corrosion stability of concrete with metakaolin in aggressive environment. Metakaolin nahrazuje část portlandského cementu v betonu. Byly studovány vlastnosti betonu, který byl uložen 60, resp. 180 dnů v korozních prostředích síranů, chloridů, hořečnatých a monných iontů. Pevnosti zkušebních těles po uloženív korozních prostředích byly porovnány s pevnostmi vzorků uložených v pitné vodě po stejnou dobu. Výsledky stanovení koeficientu korozní odolnosti představují dobrou korozní odolnost betonů s metakaolínem v agres

Czech name

Korozní odolnost betonů s vyšším obsahem metakaolínu

Czech description

Metakaolin may replace a part of Portland cement in concrete. The properties of concrete with metakaolin immersed 60 and 180 days in corrosion environments, such as chlorides, sulphates, magnesium and ammonium ions were investigated. The compressive strengths of specimens after corrosion loading were compared to the strengths of those cured in the drinking water at the same age. The results of determination of corrosion resistivity kKO present good corrosion stability of concrete with metakaolin in aggressive environment. Metakaolin nahrazuje část portlandského cementu v betonu. Byly studovány vlastnosti betonu, který byl uložen 60, resp. 180 dnů v korozních prostředích síranů, chloridů, hořečnatých a monných iontů. Pevnosti zkušebních těles po uloženív korozních prostředích byly porovnány s pevnostmi vzorků uložených v pitné vodě po stejnou dobu. Výsledky stanovení koeficientu korozní odolnosti představují dobrou korozní odolnost betonů s metakaolínem v agres

Type

D - Article in proceedings

CEP classification

JN - Civil engineering

OECD FORD branch

—

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year

2009

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection

Metakaolin 2009

ISBN

978-80-214-3843-9

ISSN

—

e-ISSN

—

Number of pages

9

Pages from-to

—

Publisher name

VUT FAST Brno

Place of publication

Brno

Event location

Brno

Event date

Mar 18, 2009

Type of event by nationality

CST - Celostátní akce

UT code for WoS article

—