Components of fracture response of alkali-activated slag mortars with steel fibres
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F18%3APU129579" target="_blank" >RIV/00216305:26110/18:PU129579 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Components of fracture response of alkali-activated slag mortars with steel fibres
Original language description
Knowledge of mechanical fracture parameters of composites based on brittle matrix is essential for the quantification of their resistance against crack initiation and propagation as well as for the definition of material models used to simulate the quasi-brittle behaviour of the structures or their parts made from this type of composites. The variability of results experimentally obtained from fracture tests of composites with different kind of fibres is much higher in comparison with composite without fibres due to the natural heterogeneity of composite containing fibres. Therefore, the main objective of this paper is to quantify the contribution of the matrix of alkali-activated slag mortars with steel fibres on their fracture response. First alkali-activated slag material was a reference without fibres; the other composites contain steel fibres in amount 5, 10, 15 and 20 % of weight of slag, respectively. The mechanical fracture parameters were determined using evaluation of fracture tests carried
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
—
OECD FORD branch
20101 - Civil engineering
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2018
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů