CHARACTERIZATION OF CEMENT-BASED COMPOSITE EXPOSED TO HIGH TEMPERATURES VIA ULTRASONIC PULSE METHOD

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F18%3APU131218" target="_blank" >RIV/00216305:26110/18:PU131218 - isvavai.cz</a>

  • Result on the web

    <a href="http://dx.doi.org/10.14311/APP.2018.15.0099" target="_blank" >http://dx.doi.org/10.14311/APP.2018.15.0099</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.14311/APP.2018.15.0099" target="_blank" >10.14311/APP.2018.15.0099</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    CHARACTERIZATION OF CEMENT-BASED COMPOSITE EXPOSED TO HIGH TEMPERATURES VIA ULTRASONIC PULSE METHOD

  • Original language description

    In this paper, the attention is paid to the investigation of the influence of high temperature acting on specimens made from specially designed cement-based composite. The experimental programme was carried out on six sets of beam specimens with the dimensions of 20 x 40 x 200 mm. The specimens were loaded to a pre-set temperature of 100, 200, 400, 600, 800 and 1000 C and then the temperature was kept for 60 minutes. When the temperature loading had been done, the specimens were left to cool down to the ambient temperature. After that, the ultrasonic pulse method was used to determine the degree of damage of temperature loaded specimens. The measured data obtained by this non-destructive method are in high correlation with values of informative compressive strength of the composite obtained after the temperature loading of specimens.

  • Czech name

  • Czech description

Classification

  • Type

    D - Article in proceedings

  • CEP classification

  • OECD FORD branch

    20101 - Civil engineering

Result continuities

  • Project

    <a href="/en/project/GA16-18702S" target="_blank" >GA16-18702S: AMIRI − Aggregate-Matrix-Interface Related Issues in silicate-based composites</a><br>

  • Continuities

    P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Others

  • Publication year

    2018

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Article name in the collection

    9th annual Conference NANO & MACRO MECHANICS 2018

  • ISBN

    978-80-01-06457-3

  • ISSN

    2336-5382

  • e-ISSN

  • Number of pages

    5

  • Pages from-to

    99-103

  • Publisher name

    Czech Technical University in Prague

  • Place of publication

    Praha

  • Event location

    Prague

  • Event date

    Sep 20, 2018

  • Type of event by nationality

    CST - Celostátní akce

  • UT code for WoS article

    000461834500018