Influence of curing conditions on mechanical and fracture properties of alkali activated slag concrete

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F19%3APU133471" target="_blank" >RIV/00216305:26110/19:PU133471 - isvavai.cz</a>

  • Result on the web

  • DOI - Digital Object Identifier

Alternative languages

  • Result language

    angličtina

  • Original language name

    Influence of curing conditions on mechanical and fracture properties of alkali activated slag concrete

  • Original language description

    The aim of this work is to determine the physical, mechanical and fracture characteristics of concrete specimens with alkali activated binder cured at different conditions. The concrete mixture with alkali activated ground granulated blast furnace slag was selected for the purpose of the experiment. The binder was activated by the liquid sodium silicate with the silicate modulus of 2.0. Natural sand and gravel were used as a fine and coarse aggregate, respectively. The maximum aggregate size was 16 mm. The binder : aggregate : water ratio was 1 : 3 : 0.46. During the specimens ageing, the dynamic modulus of elasticity was determined using a resonance method. The fracture characteristics were determined based on the results of the three-point bending test of specimens provided with an initial central edge notch. The fracture experiments were conducted at the age of 3 and 38 days. The loading force (F), the displacement measured in the middle of the span length (d), and the crack mouth opening displacem

  • Czech name

  • Czech description

Classification

  • Type

    O - Miscellaneous

  • CEP classification

  • OECD FORD branch

    20101 - Civil engineering

Result continuities

  • Project

    <a href="/en/project/GJ18-12289Y" target="_blank" >GJ18-12289Y: Advanced characterization of cracks propagation in composites based on alkali activated matrix</a><br>

  • Continuities

    P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Others

  • Publication year

    2019

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů