Bulk Zirconia Nanoceramics Prepared by Cold Isostatic Pressing and Pressureless Sintering

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F05%3APU54859" target="_blank" >RIV/00216305:26210/05:PU54859 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Bulk Zirconia Nanoceramics Prepared by Cold Isostatic Pressing and Pressureless Sintering
Original language description
Zirconia nanoparticles (stabilized by 1.5 and 3 mo.l% of yttria) with particle size below 10 nm were prepared by a sol-gel synthesis. Isostatically pressed green bodies had pore radii smaller than 5nm. After pressureless sintering at 1100C the bodies hada density exceeding 99%t.d. and grain size below 80 nm. The sintering activation energy of zirconia nanoceramics was more than twice lower than sintering activation energy of submicrometric zirconia.
Czech name
Objemová ZrO2 keramika připravená izostatickým lisováním za studena a beztlakým slinováním
Czech description
ZrO2 nanočástice (stabilizované 1,5 a 3 mol%Y2O3) s velikostí částic pod 10nm byly připraveny sol-gel syntézou. Výlisky připravené izostatickým lisováním těchto prášků měly póry o poloměru menším než 5nm. Po beztlakém slinování při 1100C měla tělesa hustotu vyšší než 99%t.h. a velikost zrn menší než 80nm. Aktivační energie slinování ZrO2 nanokeramiky byla více než dvakrát nižší než aktivační energie submikrometrického ZrO2.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JH - Ceramics, fire-proof materials and glass
OECD FORD branch
—

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)