Stability of microstructure of ultra fine-grained copper during cyclic loading

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F05%3APU65362" target="_blank" >RIV/00216305:26210/05:PU65362 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Stability of microstructure of ultra fine-grained copper during cyclic loading
Original language description
Fatigue properties, microstructural changes and strain localization in ultrafine-grained copper produced by equal channel angular pressing technique has been experimentally studied. The cyclic stress-strain response under stress control depends on the stress amplitude. The formation of shear bands resulting in fatigue crack initiation was observed both for low and high stress amplitudes.
Czech name
Stabilita mikrostruktury ultrajemnozrnné mědi během cyklického zatěžování
Czech description
Experimentálně byly studovány únavové vlastnosti, mikrostrukturní změny a lokalizace deformace v ultrajemnozrnné mědi vyrobené pomocí ECAP techniky. Cyklická napěťově deformační odezva ultrajemnozrnné mědi závisí na amplitudě napětí. Smykové pásy majícíza následek vznik únavové trhliny byly pozorovány jak při nízké tak i při vysoké hodnotě amplitudy napětí.

Project
<a href="/en/project/GD106%2F05%2FH008" target="_blank" >GD106/05/H008: Multiscale design of advanced materials</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)