Degradation of steel cable

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F07%3APU69967" target="_blank" >RIV/00216305:26210/07:PU69967 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Degradation of steel cable
Original language description
The purpose of this thesis is to determine changes in loading capacity and resistance of tow rope and track cable in uniaxial tension. These cables are exposed to damage by corrosion (NaCl and SO2). With regard to high rate of loading capacity of the cable (hundreds of kN) the thesis focuses on testing individual parts of the cable. Specifically, tensile test of rusted wires and analysis of material damage from the fractography aspect. Next, the paper deals with the design of the fixture for tensile test. In conclusion it describes the recommendation in terms of anticorrosion protection for steel ropes.
Czech name
Provozní a korozní degradace ocelových lan
Czech description
Cílem této diplomové práce je určení změny nosnosti a odolnosti tažného a nosného lana v jednoosém tahu. Tato lana jsou vystavena koroznímu poškození (NaCl a SO2). Vzhledem k vysoké hodnotě nosnosti lan (stovky kilonewtonů) je práce zaměřena na zkoušeníjednotlivých částí lana. Jedná se o tahovou zkoušku zkorodovaných drátů a analýzu poškození materiálu z hlediska fraktografie. Dále se práce zabývá návrhem upínacího modulu k tahové zkoušce. Na závěr je vypracováno doporučení v rámci protikorozní ochranyocelových lan.