Straightforward Comparison of Fatigue Crack Growth under Modes II and III
Original language description
Low-cycle fatigue crack propagation in double circumferentially notched, cylindrical specimens of austenitic steel was studied by means of special testing device in order to identify local fracture micromechanisms under remote shear modes II and III. Remote mode II crack growth rate was found to be approximately two times higher than that of the mode III. Morphological patterns on fracture surfaces revealed that the mode II and the mixed mode I + II were dominating local crack tip fracture modes operating under both remote modes II and III. No evidence of pure mode III mechanisms was detected on any investigated fracture surface.
Czech name
Přímé srovnání šíření únavových trhlin v módech II a III
Czech description
Low-cycle fatigue crack propagation in double circumferentially notched, cylindrical specimens of austenitic steel was studied by means of special testing device in order to identify local fracture micromechanisms under remote shear modes II and III. Remote mode II crack growth rate was found to be approximately two times higher than that of the mode III. Morphological patterns on fracture surfaces revealed that the mode II and the mixed mode I + II were dominating local crack tip fracture modes operating under both remote modes II and III. No evidence of pure mode III mechanisms was detected on any investigated fracture surface.
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/GA106%2F05%2F0550" target="_blank" >GA106/05/0550: Application of Quantitative Fractography and Stereology to Crack Path Analysis in Biaxial Fatigue</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
INTERNATIONAL JOURNAL OF FATIGUE
ISSN
0142-1123
e-ISSN
—
Volume of the periodical
30
Issue of the periodical within the volume
8
Country of publishing house
GB - UNITED KINGDOM
Number of pages
9
Pages from-to
—
UT code for WoS article
000256713400016
EID of the result in the Scopus database
—