Fracture Toughness of Fiber-metal Laminate CARE
Original language description
The objective of this study ia an evaluation of fracture toughness of FML consisting of carbon fibers in epoxy matrix and aluminium sheets of lay-up 6/5. Specimens with unidirectional and bidirectional orientations were tested experimentally. An effect of moisture absorption to epoxy matrix on the values of fracture toughness was reviewed in the case of UD oriented specimens.
Czech name
Lomová houževnatost vlákno-kovového laminátu CARE
Czech description
Článek obsahuje výsledky výzkumu lomové houževnatosti vlákno-kovového laminátu složeného z vrstev uhlíkového kompozitu s epoxidovou matricí s jednosměrnou a dvojsměrnou orientací vláken a vrstev hliníkové slitiny ve skladbě 6/5. Vliv absorpce vlhkosti poexpozici vlhkým teplem je ověřen na vzorcích s UD uspořádáním.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JI - Composite materials
OECD FORD branch
—

Project
<a href="/en/project/1M0501" target="_blank" >1M0501: Aerospace Research Centre</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)