EXPERIMENTAL VERIFICATION OF A MODEL OF STEEL REOXIDATION
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F09%3APU80291" target="_blank" >RIV/00216305:26210/09:PU80291 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
čeština
Original language name
Experimentální ověření modelu reoxidace
Original language description
Reoxidation of steel is a term for summary designation of secondary and tertiary oxidation of steel occurring during keeping the metal in a ladle after tapping it from a furnace and during casting in a mould cavity. During reoxidation the oxygen concentration and its activity in a casting are growing. In case that oxygen activity exceeds the equilibrium activity of oxygen with carbon the casting part or the whole casting can be afflicted with gas cavities of carbon monoxide. With higher oxygen activitythe formations of oxides of elements with lower deoxidation ability (Mn, Si) continues. Those oxides can form in castings the extensive slaggy formations in their volume or on the casting surface designated as secondary slag inclusions. Thus the steel reoxidation directly influences surface and internal quality of steel castings and consequently the manufacturing costs too.
Czech name
Experimentální ověření modelu reoxidace
Czech description
Reoxidation of steel is a term for summary designation of secondary and tertiary oxidation of steel occurring during keeping the metal in a ladle after tapping it from a furnace and during casting in a mould cavity. During reoxidation the oxygen concentration and its activity in a casting are growing. In case that oxygen activity exceeds the equilibrium activity of oxygen with carbon the casting part or the whole casting can be afflicted with gas cavities of carbon monoxide. With higher oxygen activitythe formations of oxides of elements with lower deoxidation ability (Mn, Si) continues. Those oxides can form in castings the extensive slaggy formations in their volume or on the casting surface designated as secondary slag inclusions. Thus the steel reoxidation directly influences surface and internal quality of steel castings and consequently the manufacturing costs too.
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/FT-TA5%2F048" target="_blank" >FT-TA5/048: Prediction and elimination of inner and surface defects of produts into foundry processing</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2009
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Transaction of the VŠB-Technical university of Ostrava, Mechanical series
ISSN
1210-0471
e-ISSN
—
Volume of the periodical
52
Issue of the periodical within the volume
2
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
8
Pages from-to
—
UT code for WoS article
—
EID of the result in the Scopus database
—