Stress distribution along the 3D crack front
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F09%3APU83776" target="_blank" >RIV/00216305:26210/09:PU83776 - isvavai.cz</a>
Alternative codes found
RIV/68081723:_____/09:00332522
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Stress distribution along the 3D crack front
Original language description
For fracture specimens of finite thickness, the stress-state in the region where the crack front intersects the free surfaces orthogonally is still an unsolved issue. The authors of the contribution focused on the problem of stress distribution through the thickness of elastic body from three various analytical concepts. The effect of Poisson's ratio on the calculated fracture parameters is examined. Variations of the stress intensity factors, T-stress and generalized stress intensity factors with thickness of the edge cracked plates are presented. The physical significance of the results is discussed and the phenomena observed are explained.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2009
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů