Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU93216" target="_blank" >RIV/00216305:26210/11:PU93216 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC

Original language description

This paper is focused on the study of initiation and growth of fatigue cracks in IN713LC with Al protective coating and without coating. Microstructure characteristics and microhardness of Al coating are documented. Fatigue crack initiation and fatigue crack growth mechanisms were identified. The crack propagation rates were obtained based on striation spacing in fracture surfaces.

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JG - Metallurgy, metal materials

OECD FORD branch

—

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Publication year

2011

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Chemické listy

ISSN

0009-2770

e-ISSN

—

Volume of the periodical

105

Issue of the periodical within the volume

—

Country of publishing house

CZ - CZECH REPUBLIC

Number of pages

2

Pages from-to

840-841

UT code for WoS article

—

EID of the result in the Scopus database

—