Original industrial application of two numerical models in concasting technology
Original language description
This paper deals with the causes of a transversal crack in a steel slab with an l300 ,l45 mm cross-section by means of results from two models. Samples were taken from and around the crack in order to analyze the concentration (chemical heterogeneity) of the selected elements. Simultaneously, the concentration of elements at the surface of the crack was measured after the crack was opened. The chemical heterogeneity of elements was analyzed by means of the JEOL JXA 8600/KEVEX analytical equipment. The measurement results were processed using mathematical statistics procedures. The results proved that there was an internal crack initiating immediately below the curve of the solid-state temperature and consecutively propagating.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)