CYCLIC DEFORMATION RESPONSE OF AZ31 MAGNESIUM ALLOY AFTER CORROSION DEGRADATION

Original language description

Cyclic deformation response and low cycle fatigue behaviour of bare and pre-corroded magnesium alloy AZ31 was studied under stress amplitude control. Pre-corroded specimens had been exposed to spray of 5 % solution of sodium chloride for 480 and 1000 hours. Fatigue limit drops from 52.1 Mpa to 47.5 MPa (480 hrs) and 38.4 (1000 hrs). Fatigue life decrease due to corrosion damage is pronounced at loww stress amplitudes, whereas the durability attained at higher amplitudes is practically the same.

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JG - Metallurgy, metal materials

OECD FORD branch

—

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Publication year

2011

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Chemické listy

ISSN

0009-2770

e-ISSN

—

Volume of the periodical

105

Issue of the periodical within the volume

S

Country of publishing house

CZ - CZECH REPUBLIC

Number of pages

3

Pages from-to

787-789

UT code for WoS article

—

EID of the result in the Scopus database

—