Fatigue strength of weathering steel ATMOFIX 52A

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU96270" target="_blank" >RIV/00216305:26210/11:PU96270 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Fatigue strength of weathering steel ATMOFIX 52A
Original language description
Deterioration of fatigue properties of weathering steels is a serious problem of operating life of engineering components subjected to corrosion and cyclic loads. There are two possible mechanisms of damage, which are discussed in literature. There is aneffect of surface roughening, which develops during corrosion, and an effect of corrosion cracks, which can influence the fatigue crack initiation. The paper contains results of an experimental determination of fatigue life of ATMOFIX 52A grade steel with a corroded surface and comparison with the fatigue strength of basic smooth material. The notch effect of corrosion dimples, which initiated fatigue cracks, was determined on the basis of fractographic observation and numerical evaluation of stress concentration. It has been found that the reduction of the fatigue life can be quantitatively well predicted by means of the fatigue notch effect of corrosion dimples. No risky corrosion cracks were found in the studied corroded material.
Czech name
—
Czech description
—

Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
13th Conference Applied Mechanics 2011
ISBN
978-80-87434-03-1
ISSN
—
e-ISSN
—
Number of pages
4
Pages from-to
127-130
Publisher name
Institute of Physics of Materials, Academy of Sciences of the Czech Republic
Place of publication
Brno
Event location
Velké Bílovice
Event date
Apr 18, 2011
Type of event by nationality
EUR - Evropská akce
UT code for WoS article
—

Similar results(10)