The effect of residual stresses on crack shape in polymer pipes
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F12%3APU102295" target="_blank" >RIV/00216305:26210/12:PU102295 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
The effect of residual stresses on crack shape in polymer pipes
Original language description
The effect of residual stresses on crack geometry and consequently on crack behaviour in polymer pipes is estimated. Crack geometry has a significant influence on the resulting stress intensity factor value. The shape of a crack in three-dimensional analysis was numerically estimated using a special routine which ensures constant stress intensity factor along the crack front. It was found that the crack shape was influenced by the presence of residual stresses and significant increase of the stress intensity factor for a pipe with residual stresses in comparison with a pipe without residual stresses was observed. An approximative equation for stress intensity factor estimation in a pipe with residual stresses was presented and its accuracy tested.
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2012
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Proceedings of the 4th International Conference on CRACK PATHS (CP 2012)
ISSN
2281-1060
e-ISSN
—
Volume of the periodical
1
Issue of the periodical within the volume
1
Country of publishing house
IT - ITALY
Number of pages
8
Pages from-to
489-496
UT code for WoS article
—
EID of the result in the Scopus database
—