Evaluation of fatigue life of AZ31 magnesium alloy fabricated by squeeze casting

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F13%3APU100070" target="_blank" >RIV/00216305:26210/13:PU100070 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Evaluation of fatigue life of AZ31 magnesium alloy fabricated by squeeze casting

Original language description

Cyclic deformation behavior and fatigue life of squeeze-cast AZ31 magnesium alloy was studied under stress amplitude-control at room temperature. Low and high cycle fatigue tests with engineering stress amplitudes in the range from 40 to 110 MPa were conducted. Analysis of hysteresis curves was performed. Tension–compression asymmetry of hysteresis loops was not observed; the alloy exhibited cyclic hardening in tension and compression. The fatigue life in the low cycle fatigue region was expressed by Wöhler and derived Manson–Coffin curves. Experimental data in both, the low and high cycle fatigue regions were fitted by means of regression functions. S–N curves exhibited a smooth transition from the low to the high cycle fatigue regions and significant scattering of experimental points was observed. Furthermore, metallographic and fractographic analyses were performed. Crack initiation occurred from the specimen surface or on clusters of secondary particles; the region of final fracture was characterized by a transgranular ductile fracture. It can be concluded that the fatigue properties of squeeze cast magnesium alloy AZ31 are significantly improved comparing to materials prepared by common methods of casting. Squeeze casting also enables the cost-effective fabrication of complicatedly shaped parts.

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JG - Metallurgy, metal materials

OECD FORD branch

—

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year

2013

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Materials and design

ISSN

0261-3069

e-ISSN

—

Volume of the periodical

45

Issue of the periodical within the volume

3

Country of publishing house

US - UNITED STATES

Number of pages

12

Pages from-to

253-264

UT code for WoS article

—

EID of the result in the Scopus database

—