Investigation of Changes in Microstructure of Remelted Air Plasma Sprayed NiCrAlY Coating after Thermal Exposure in Air with the Assistance of Microhardness Measurements
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU107790" target="_blank" >RIV/00216305:26210/14:PU107790 - isvavai.cz</a>
Result on the web
<a href="http://www.scientific.net/KEM.586.226" target="_blank" >http://www.scientific.net/KEM.586.226</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.586.226" target="_blank" >10.4028/www.scientific.net/KEM.586.226</a>
Alternative languages
Result language
angličtina
Original language name
Investigation of Changes in Microstructure of Remelted Air Plasma Sprayed NiCrAlY Coating after Thermal Exposure in Air with the Assistance of Microhardness Measurements
Original language description
In present work, the NiCrAlY coatings were sprayed onto the surface of nickel-based superalloy INCONEL 713LC substrates by means of conventional air plasma spray technique. Subsequently an aluminium sheet was cladded onto the coating surface by means of uniaxial cold pressing. The samples prepared by this way were annealed at the temperatures of 650, 850 and 1000oC for two hours in argon-flow atmosphere. NiCrAlY coatings were enriched by aluminium and the coating imperfections presented in a coating were eliminated. The remelted NiCrAlY coating specimens were annealed at a temperature of 800oC for fifty hours in ambient atmosphere. The microstructural changes and phase transformations after short thermal exposure in air of the remelted NiCrAlY plasma sprayed coatings were observed. Generally, a change was observed in the phase composition of remelted coatings from phases rich in aluminium to phases less rich in aluminium owing to thermal exposure in air. The increase in the microhardness of the whole remelted coating after thermal exposure was caused by the increase in the amount of Al3Ni2 intermetallic phase in the remelted coating.
Czech name
—
Czech description
—
Classification
Type
D - Article in proceedings
CEP classification
—
OECD FORD branch
20506 - Coating and films
Result continuities
Project
<a href="/en/project/GAP107%2F12%2F1922" target="_blank" >GAP107/12/1922: Thermal Spray Processing and High Temperature Structural Stability of Nanocrystalline Thermal Barrier Coatings</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Article name in the collection
Key Engineering Materials
ISBN
9783037859346
ISSN
1013-9826
e-ISSN
—
Number of pages
4
Pages from-to
226-229
Publisher name
Trans Tech Publications Ltd
Place of publication
Zurich-Durnten, Switzerland
Event location
Brno
Event date
Jul 1, 2013
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
000336633500055