Formation of Intermetallic Phases in Fe-Al Binary Cold Spray Thick Deposit

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU109519" target="_blank" >RIV/00216305:26210/14:PU109519 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Formation of Intermetallic Phases in Fe-Al Binary Cold Spray Thick Deposit
Original language description
Deposits of 60/40 at% Fe/Al were produced by low-pressure cold spray technique using heated air (300C, 15 bar) as working gas.Samples of the deposited material were then annealed isothermally at temperatures from 250C to 750C for two hours in argon protective atmosphere. Gradual evolution of intermetallic phases by diffusion mechanism at temperatures from 550C was observed. The evolved phases included metastable and stable phases close to Al3Fe, FeAl, Al5Fe2 and Al2Fe. The samples general shape was preserved during the heating process due to a rapid formation of intermetallic skeleton (at temperatures exceeding aluminum melting temperature).
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
International Thermal Spray Conference 2014 Proceedings
ISBN
978-3-87155-574-9
ISSN
—
e-ISSN
—
Number of pages
4
Pages from-to
908-912
Publisher name
DVS Media GmbH
Place of publication
Barcelona, Španělsko
Event location
Barcelona
Event date
May 21, 2014
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
—

Similar results(10)