Dwell effects on low cycle fatigue behaviour of diffusion coated nickel base superalloy IN 713LC at temperature of 800°C
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F15%3APU114066" target="_blank" >RIV/00216305:26210/15:PU114066 - isvavai.cz</a>
Alternative codes found
RIV/68081723:_____/15:00444732
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Dwell effects on low cycle fatigue behaviour of diffusion coated nickel base superalloy IN 713LC at temperature of 800°C
Original language description
Materials used for high temperature applications such as disks, blades and vanes of gas turbine engines require exceptional resistance to mechanical and thermal loading as well as against chemical attacks by oxidation, which significantly increases withoperating temperature. First generation Ni-base superalloy IN 713LC developed by the International Nickel Company in the 1950s is the representative of cast materials used for these purposes, especially because of favorable price in conjunction with satisfying high temperature properties. However, the continuous enhancing of operating temperature severely degrades the material surface and adversely affects the strength properties and component life. Protection of the surface and prevention of its degradation is a major goal of today and tomorrow. Diffusion coatings are primarily used to safeguard the material from aggressive environments and to improve corrosion and oxidation stability of surface. Nowadays, superalloy surface is enriche
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů