NANOSCALE PHASES ON SURFACE FE-6SI MAGNETIC SHEETS
Original language description
Analysis of the nanoscale phases which appear on the surface Fe-6Si samples were carried out after the various treatments -grinding and etching, annealing, and water jet abrasion. The basic information on structure, chemical and phase composition was obtained by X-Ray Powder Diffraction (XRD), Scanning Electron Microscopy with EDX, Glow Discharge Optical Emission Spectrometry (GDOES), Mssbauer Spectroscopy and X-ray Photoelectron Spectrometry (XPS). The results show high stability of the surface phase composition after the mechanical and heat treatments. Results obtained from the surface analysis in micrometer depth (XRD, EDX, GDOES) do not show any changes after the different treatments. Iron oxides were detected in XPS and conversion electron Mssbauer spectra (CEMS) which analyze the surface composition in a nanometer scale. In addition to, fine changes in atomic ordering on the surface can be observed after mechanical and heat treatments in the CEMS spectra.
Czech name
—
Czech description
—

Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)