Poling procedures and piezoelectric response of (Ba0.85Ca0.15Zr0.1T0.9)O-3 ceramics

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F20%3APU138309" target="_blank" >RIV/00216305:26220/20:PU138309 - isvavai.cz</a>
Result on the web
<a href="https://www.tandfonline.com/doi/full/10.1080/21870764.2020.1860438" target="_blank" >https://www.tandfonline.com/doi/full/10.1080/21870764.2020.1860438</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1080/21870764.2020.1860438" target="_blank" >10.1080/21870764.2020.1860438</a>

Result language
angličtina
Original language name
Poling procedures and piezoelectric response of (Ba0.85Ca0.15Zr0.1T0.9)O-3 ceramics
Original language description
The goal of the current report was to find the optimal poling conditions: poling field, poling time and poling temperature for lead-free (Ba0.85Ca0.15Zr0.1T0.9)O-3 ceramic. It has been noticed that the low poling field (< 2 kV/mm) was insufficient for obtaining ideal poling state (theta = 90 degrees) due to the incomplete switching of domains and thus low piezoelectric properties (d(33) <= 438 pC/N and k(p) <= 49%). However, relevance of higher poling voltage (> 2 kV/mm) may induce electric breakdown and physical defects such as cracks in the sample, which also leads degradation of piezoelectric properties. The optimal poling field, poling time and poling temperature was found to be 2 kV/mm, 10 min and 24 degrees C, i.e., near room temperature, respectively to achieve nearly ideal poling state (theta = 86 degrees) obtained by impedance spectra, and thus enhanced piezoelectric constant d(33) = 505 pC/N and k(p) = 56% at room temperature. The O-T phase transition point was identified at 32.6 degrees C, for which a peak value of d(33(E=0V)) = 622 pm/V was realized.
Czech name
—
Czech description
—

Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20504 - Ceramics

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2020
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)