XRD analysis of chemical composition on lead surface microelectrodes
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F21%3APU140795" target="_blank" >RIV/00216305:26220/21:PU140795 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
XRD analysis of chemical composition on lead surface microelectrodes
Original language description
This work is focused on the observation of changes in the chemical composition on the surface of the negative electrode of the lead-acid battery using an XRD diffractometer. The measurement was performed on thin pasted electrodes with a thickness of about 1mm. After the maturation and molding process, the fully charged negative electrode was gradually discharged and charged at a rate of 0.2 C and 0.3 C. The negative electrode was analyzed at 100 %, 80 %, 60 %, 40 % 20 % a 0 % SOC states. Chemical changes occurring on the surface of the negative electrode during discharging and charging of the lead-acid battery were measured using X-ray diffractometer Rigaku MiniFlex HR 600.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
—
OECD FORD branch
10405 - Electrochemistry (dry cells, batteries, fuel cells, corrosion metals, electrolysis)
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2021
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů