Morphology study of 2-ethylhexyl acrylate/cellulose acetate propionate microcapsules prepared via solvent evaporation technique

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F17%3APU124424" target="_blank" >RIV/00216305:26310/17:PU124424 - isvavai.cz</a>

  • Result on the web

  • DOI - Digital Object Identifier

Alternative languages

  • Result language

    angličtina

  • Original language name

    Morphology study of 2-ethylhexyl acrylate/cellulose acetate propionate microcapsules prepared via solvent evaporation technique

  • Original language description

    Novel 2-ethylhexyl acrylate (2-EHA)/cellulose acetate propionate (CAP) microcapsules with mononuclear core-shell morphology are potentially an interesting model system for polymerization inside microcapsules. Microencapsulation was performed by solvent evaporation technique from dichloromethane solution dispersed in poly(vinyl alcohol) solution. Microcapsule morphology, which evolved from partially raspberry-like to a bowl like due to premature shell formation and subsequent solvent evaporation, was captured by microscopy imaging techniques. Thus it has been concluded that kinetics of CAP shell formation play a crucial role in preparation of 2 EHA/CAP microcapsules. Moreover, microcapsules were ruptured in compression under microscope in order to evaluate fracture type. Ductile fracture of microcapsule shell was observed. Shell thickness of 0.3 μm was estimated by scanning electron microscopy. Even though bowl-like morphology of microcapsules was not favorable for polymerization inside microcapsules,

  • Czech name

  • Czech description

Classification

  • Type

    O - Miscellaneous

  • CEP classification

  • OECD FORD branch

    10404 - Polymer science

Result continuities

  • Project

  • Continuities

    S - Specificky vyzkum na vysokych skolach

Others

  • Publication year

    2017

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů