Failure Analysis of Spheric Roller Bearing
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F13%3APU107875" target="_blank" >RIV/00216305:26620/13:PU107875 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Failure Analysis of Spheric Roller Bearing
Original language description
The failure of a spherical-roller bearing consisting of spherical rollers, outer and inner rings made of 100CrMn6 steel was studied. After a trial test, in which several spherical rollers were completely destroyed and a long continuous radial crack appeared in the outer ring, pitting degradation was observed on all bearing parts. The bearing components were studied (separately) by means of light and electron microscopy. The chemical composition was estimated by means of glow discharge optical emission spectroscopy. X-ray diffraction was utilized for qualitative and quantitative phase analyses. As a representative of mechanical properties, the hardness was also measured.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/ED1.1.00%2F02.0068" target="_blank" >ED1.1.00/02.0068: Central european institute of technology</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů