Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F16%3APU119776" target="_blank" >RIV/00216305:26620/16:PU119776 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170
Original language description
The aim of this analysis was to identify the cause of poor corrosion resistance of final product, after the slight change of heat treatment of initial material. Although the hardness of material prior and after the change was the same, significant difference in microstructure was revealed by microstructural analysis. Change in heat treatment process lead to heterogeneous distribution of precipitates and increase in the precipitate size which caused deterioration in corrosion resistance. Based on the findings, further optimization of heat treatment was suggested. More importantly, initial material inspection based on microstructural analysis, not only mechanical testing, was recommended. recommended.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů