Stress Intensity Factors for Rough Cracks Loaded in Mode II
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F16%3APU120842" target="_blank" >RIV/00216305:26620/16:PU120842 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Stress Intensity Factors for Rough Cracks Loaded in Mode II
Original language description
Most fracture mechanical models do not take the materials microstructure into account and use averaged material properties although the real crack flanks and fronts exhibit microstructurally induced tortuous shapes. These influences the stress-strain field at the crack front as well as the related stress intensity factors. This phenomenon was investigated by some authors only for remote mode I loading and was named geometrically induced shielding. This study is focused on the analysis of the stress intensity factors for rough cracks loaded in the shear mode II by modelling the Compact-Tension-Shear specimen containing cracks of various roughness.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Others
Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů