Oxidation of Experimental Ti-Si-Al Based Alloys
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F16%3APU121328" target="_blank" >RIV/00216305:26620/16:PU121328 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Oxidation of Experimental Ti-Si-Al Based Alloys
Original language description
Despite the fact that conventional high temperature titanium alloys possess a good combination of low weight, high strength and good corrosion resistance, their operational temperatures do not exceed 540-600 °C, since at higher temperatures they suffer from extensive oxidation, scaling and formation of a brittle oxygen-reach diffusion layer on their surface, so-called apha-case’. The alloying with silicon was regarded as a promising way to raise the working temperatures of titanium alloys, since silicon is known to improve oxidation resistance, oxide scale adherence and high temperature creep behavior of titanium without noticeable deterioration of its ductility. The present paper was focused on studying of the oxidation kinetics and the formation of oxide scale and alpha-case layers on a series of experimental Ti-Al-Si based alloys, additionally alloyed with zirconium and tin. The oxidation kinetics of the experimental alloys upon exposure in air at 700 °С for up to 240 hours was examined and compar
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů