Analysis of Surface Layer Defects on Carburezed Steel Component after Alkaline Blackening

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F17%3APU122957" target="_blank" >RIV/00216305:26620/17:PU122957 - isvavai.cz</a>
Result on the web
<a href="http://www.scientificnet/MSF.891.274" target="_blank" >http://www.scientificnet/MSF.891.274</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientificnet/MSF.891.274" target="_blank" >10.4028/www.scientificnet/MSF.891.274</a>

Result language
angličtina
Original language name
Analysis of Surface Layer Defects on Carburezed Steel Component after Alkaline Blackening
Original language description
Alkaline blackening is one of the most popular surface treatment technology of components with the requirement for higher surface corrosion resistance, increased hardness, and the decorative appearance. This contribution deals with the appearance of surface defects on carburized steel components after the process of alkaline blackening, which appeared to be red shiny stains on an otherwise black matte surface of the component. The occurrence of defects on surface was observed several days after the alkaline blackening process. By means of metallographic methods, direct connection between surface defects and the microstructure of the material was found. Contribution further deals with the influence of microstructure and technological parameters on the quality of the final surface layer of the components.
Czech name
—
Czech description
—

Project
<a href="/en/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)