Failure analysis of massively failed compressed air cartridge
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F17%3APU124346" target="_blank" >RIV/00216305:26620/17:PU124346 - isvavai.cz</a>
Result on the web
<a href="https://doi.org/10.1016/j.engfailanal.2017.07.016" target="_blank" >https://doi.org/10.1016/j.engfailanal.2017.07.016</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.engfailanal.2017.07.016" target="_blank" >10.1016/j.engfailanal.2017.07.016</a>
Alternative languages
Result language
angličtina
Original language name
Failure analysis of massively failed compressed air cartridge
Original language description
Aim of the analysis was to determine the cause of massive failure of compressed air cartridge in respect to used material, quality of stock, its chemical composition, mechanical properties and quality of inner surface of the component. Furthermore, comparative analysis of identical component fabricated prior to innovation of fabrication technology was carried out. The study describes corrosion attack documented on the component – pitting corrosion and evaluates connection between its appearance and microstructure of used material, surface quality, change in design and presence or lack of surface treatment namely anodic oxidation. Part of the analysis is a theoretical calculation of the real load applied on compressed air cartridge, with respect to state and quality on inner surface, in real operating conditions. Light microscopy and scanning electron microscopy techniques were used for microstructural assessment as well as fractographic analysis.
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20506 - Coating and films
Result continuities
Project
<a href="/en/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
ENGINEERING FAILURE ANALYSIS
ISSN
1350-6307
e-ISSN
1873-1961
Volume of the periodical
neuveden
Issue of the periodical within the volume
82
Country of publishing house
GB - UNITED KINGDOM
Number of pages
7
Pages from-to
776-782
UT code for WoS article
000413323400067
EID of the result in the Scopus database
2-s2.0-85026363819