Processing and properties of luminescent Cr3+ doped transparent alumina ceramics

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F20%3APU136253" target="_blank" >RIV/00216305:26620/20:PU136253 - isvavai.cz</a>

  • Result on the web

    <a href="https://www.sciencedirect.com/science/article/pii/S0955221919307575" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0955221919307575</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2019.11.010" target="_blank" >10.1016/j.jeurceramsoc.2019.11.010</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    Processing and properties of luminescent Cr3+ doped transparent alumina ceramics

  • Original language description

    Transparent Cr2O3-doped alumina ceramics were prepared by slip casting, followed by pre-sintering in ambient atmosphere and hot isostatic pressing. The effect of dopant concentration on material properties, including microstructure and optical properties was evaluated. Real in-line transmittance in the range of 20–44 % was measured for the ceramics with the mean grain size<520 nm: the transmittance decreased with increasing grain size and Cr content. The excitation spectra consisted of two broad bands with maxima at 404 nm and 558 nm, corresponding to 4A2g→4T1g and 4A2g→4T2g transitions of Cr3+ ions in octahedral sites of α-Al2O3. The intensive deep red narrow emissions under violet/green light excitation, R-lines (2Eg→4A2g transition), were observed at 692.5 nm and 693.8 nm, that are very close to ruby single crystal. The highest emission was achieved at the Cr3+ concentration of 0.4 at.%. The luminescence decay curves exhibited single-exponential behaviour with decay times of ∼3.6 ms.

  • Czech name

  • Czech description

Classification

  • Type

    J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database

  • CEP classification

  • OECD FORD branch

    20504 - Ceramics

Result continuities

  • Project

    Result was created during the realization of more than one project. More information in the Projects tab.

  • Continuities

    P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Others

  • Publication year

    2020

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Name of the periodical

    Journal of the European Ceramic Society

  • ISSN

    0955-2219

  • e-ISSN

    1873-619X

  • Volume of the periodical

    40

  • Issue of the periodical within the volume

    7

  • Country of publishing house

    GB - UNITED KINGDOM

  • Number of pages

    8

  • Pages from-to

    2573-2580

  • UT code for WoS article

    000523618300009

  • EID of the result in the Scopus database

    2-s2.0-85075433031