Viscous flow spark plasma sintering of glass microspheres with YAG composition and high tendency to crystallization
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F21%3APU141739" target="_blank" >RIV/00216305:26620/21:PU141739 - isvavai.cz</a>
Result on the web
<a href="https://www.sciencedirect.com/science/article/pii/S0955221920308281?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0955221920308281?via%3Dihub</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2020.10.015" target="_blank" >10.1016/j.jeurceramsoc.2020.10.015</a>
Alternative languages
Result language
angličtina
Original language name
Viscous flow spark plasma sintering of glass microspheres with YAG composition and high tendency to crystallization
Original language description
Present work is focused on the preparation of bulk glass with stoichiometric yttrium aluminium garnet (YAG) composition, which has high tendency to crystallize. Glass microspheres were prepared by flame synthesis from sol-gel prepared YAG precursor. Sintering conditions in SPS apparatus such as heating rate, pressure and temperature were optimized with the aim to prepare transparent material. Results revealed that glass with high tendency to crystallize is very sensitive to time of densification under load (associated with the maximum applied temperature). The increase of the pressure led to the expansion of the translucent part of the sample. Dense, and slightly translucent amorphous samples (total transmission measured at 550 nm was 4.8 %) were successfully prepared by viscous flow SPS sintering of glass microspheres at temperatures below 910 degrees C without any isothermal dwell.
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20504 - Ceramics
Result continuities
Project
<a href="/en/project/LTT18013" target="_blank" >LTT18013: Development of functional ceramic and glass ceramic materials in collaboration with the Centre of Excellence FunGlass</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2021
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
ISSN
0955-2219
e-ISSN
1873-619X
Volume of the periodical
41
Issue of the periodical within the volume
2
Country of publishing house
GB - UNITED KINGDOM
Number of pages
6
Pages from-to
1537-1542
UT code for WoS article
000599860500004
EID of the result in the Scopus database
2-s2.0-85092708093