Transparent LiOH-doped magnesium aluminate spinel produced by spark plasma sintering: Effects of heating rate and dopant concentration

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F23%3APU148617" target="_blank" >RIV/00216305:26620/23:PU148617 - isvavai.cz</a>

  • Result on the web

    <a href="https://www.sciencedirect.com/science/article/pii/S0955221923000729" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0955221923000729</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2023.01.059" target="_blank" >10.1016/j.jeurceramsoc.2023.01.059</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    Transparent LiOH-doped magnesium aluminate spinel produced by spark plasma sintering: Effects of heating rate and dopant concentration

  • Original language description

    The effects of LiOH doping of magnesium aluminate spinel powders and various Spark Plasma Sintering (SPS) schedules on densification behavior and final transparency of polycrystalline magnesium aluminate spinel were studied. Two commercial magnesium aluminate spinel powders, with different specific surface areas, were doped with up to 0.6 wt% of LiOH and consolidated using SPS with slow (2.75 degrees C/min) and fast (100 degrees C/min) heating rates. The slow heating rate was optimal for undoped magnesium aluminate spinel (LiOH-free) with the best real in-line transmittance (RIT) of 84.8% (measured at 633 nm on a disc 0.8 mm thick). For the magnesium aluminate spinel doped with 0.3 wt% of LiOH, the fast heating rate was beneficial, and an RIT of 76.5% was achieved. mu-Raman analysis confirmed that the addition of LiOH suppressed carbon contamination.

  • Czech name

  • Czech description

Classification

  • Type

    J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database

  • CEP classification

  • OECD FORD branch

    20504 - Ceramics

Result continuities

  • Project

    Result was created during the realization of more than one project. More information in the Projects tab.

  • Continuities

    P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Others

  • Publication year

    2023

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Name of the periodical

    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY

  • ISSN

    0955-2219

  • e-ISSN

    1873-619X

  • Volume of the periodical

    43

  • Issue of the periodical within the volume

    8

  • Country of publishing house

    GB - UNITED KINGDOM

  • Number of pages

    9

  • Pages from-to

    3544-3552

  • UT code for WoS article

    000955301200001

  • EID of the result in the Scopus database

    2-s2.0-85147356151