SERVICE LIFE OF HOT DIP GALVANIZED STEEL CONSTRUCTION

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25794787%3A_____%2F05%3A%230000018" target="_blank" >RIV/25794787:_____/05:#0000018 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
SERVICE LIFE OF HOT DIP GALVANIZED STEEL CONSTRUCTION
Original language description
Atmospheric environment containing air pollutants causes damage of materials, technice! objects and detection systems. In last decade SO2 pollution significantly decreased in Europe induding Central Burope. It means the corrosion rate of all structural materials decreased too. Decreasing SO2 affected the corrosion rate of zinc significantly. On base of UNECE ICP program, the dose/response functions for many materials including zinc were derived. This dose/resppnse function was used for mapping corrosionrate of zinci in Czech Republic.
Czech name
Životnost konstrukcí s žárovým zinkovým povlakem
Czech description
Atmoférické prostředí obsahující znečištění vyvolává poškození materiálů, technických objektů a ochranných systémů. V posledním desetiletí se v Evropě včetně střední Evropy významně snížilo znečištění SO2. To ovlivnilo korozní rychlost všech konstrukčních kovů. Nejvíce se toto snížení projevilo u zinku. Na základě výsledků UNECE ICP programu byly pro mnoho materiály včetně zinku odvozeny dose/response rovnice. Tato rovnice byla použita pro mapování korozní rychlosti zinku v ČR.