Creep Resistance of 0.5Cr-0.5Mo-0.3V Steel Weldments after 162 kh Operation

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F07%3A%230000053" target="_blank" >RIV/25797000:_____/07:#0000053 - isvavai.cz</a>
Alternative codes found
RIV/25797000:_____/07:#0000158
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Creep Resistance of 0.5Cr-0.5Mo-0.3V Steel Weldments after 162 kh Operation
Original language description
The work brings the results of a study performed with the specimens from a pipe made of low alloy steel of type 0.5Cr-0.5Mo-0.3V (ČSN 15123.5, 14MoV6-3). Sufficiently long term creep rupture properties of the weld joint operated for 162 kh at a temperature of 540°C and pressure of 13.52 MPa are compared with the material of regenerated properties. The work makes it possible to evaluate the service life of the pipeline.
Czech name
Creepová odolnost svarového spoje oceli 0,5Cr-0,5Mo-0,3V po 162 000 hodinách provozu.
Czech description
Práce přináší výsledky studia provedené na trubce z oceli 0,5Cr-0,5Mo-0,3V (ČSN 15123.5, 14MoV6-3). Dostatečně dlouhé creepové zkoušky svarového spoje po 162 000 h provozu při teplotě 540°c a tlaku 13,52MPa byly porovnány s regenerovaným materiálem. Práce umožňují stanovit provozní životnost putrubního systému.