Effect of carbide size in hardfacing on abrasive wear
Original language description
Abrasive wear of high alloyed overlay materials with high contents of carbide phases of M7C3 depends on the sizes of the carbide particles and on their distribution in an overlay. This work is focused on the study of the carbide particles size effect onabrasive wear. The size of carbide particles of M7C3 type, their distribution (part) in the matrix and their effect on abrasive wear were measured. Hardness in single layers, as well as microhardness of the matrix and of carbide particles, were also measured. The abrasive wear resistance was measured using the pin-on-disk machine with bonded abrasive particles. For the study of the chemical composition, the scanning electron microscopy with energy dispersive X-ray analysis (EDX) was used.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/GP101%2F07%2FP124" target="_blank" >GP101/07/P124: Degradation substratum of welding surface</a><br>
Continuities
N - Vyzkumna aktivita podporovana z neverejnych zdroju

Publication year
2009
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)