Investigation of mechanical properties and microstructure of X60 line-pipe steel

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F19%3AN0000056" target="_blank" >RIV/25797000:_____/19:N0000056 - isvavai.cz</a>
Alternative codes found
RIV/68407700:21220/19:00349602
Result on the web
<a href="https://www.sciencedirect.com/science/article/pii/S2452321619302355" target="_blank" >https://www.sciencedirect.com/science/article/pii/S2452321619302355</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.prostr.2019.08.031" target="_blank" >10.1016/j.prostr.2019.08.031</a>

Result language
angličtina
Original language name
Investigation of mechanical properties and microstructure of X60 line-pipe steel
Original language description
A segment of seam pipeline with an outer diameter (OD) 813 mm and wall thickness (WT) 10,6 mm, operating since 1974, was used for investigation of its mechanical properties and microstructure. The results of the tensile test show that nominal values of minimum yield point, ultimate tensile strength and ductility were reached in all specimens. Charpy V-notch test was carried out on base metal, heat affected zone and seam weld at temperatures 40, 20, 0, -20, -40 and -60 °C. In case of base metal, L-T orientation showed higher upper shelf energy (USE) and ductile-brittle transition temperature (DBTT) than T-L orientation than is typical for hot-rolled material. The lowest impact energy was measured in the heat affected zone and seam weld due to the presence of heterogeneous microstructure consisting of grain boundary ferrite, polygonal ferrite and Widmanstätten ferrite.
Czech name
—
Czech description
—

Project
—
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace<br>N - Vyzkumna aktivita podporovana z neverejnych zdroju

Publication year
2019
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)