Materialographic Analysis of MAR M-247 Superalloy
Original language description
This paper presents the results of structural phase analysis of MAR-M247 superalloy. Analysis was performed at initial and in as casted state after various type of solution annealing in the range 900 °C to 1240 °C with cooling in water. Presented polycrystalline alloy is heat resisting nickel superalloy, especially usable for highly strained components in the industry producing stationary gas turbines and aircraft engines. Analysis was performed using of a Quanta FEG 450 scanning electron microscope with micro-analytic system Trident APEX-4 which have identified presented minor phase. Attention was also paid to its eventual changes after different type of solution annealing.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/LO1203" target="_blank" >LO1203: Regional Materials Science and Technology Centre - Feasibility Program</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)