Medium karbon steel processed by warm Equal Channel Angular Pressing

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F06%3A%230000016" target="_blank" >RIV/26316919:_____/06:#0000016 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Medium karbon steel processed by warm Equal Channel Angular Pressing
Original language description
The present work deals with grain refinement of medium carbon steel. The structure refinement was conducted in two steps. Preliminary refinement was achieved by multistep open forging and further grain refinement was accomplished during warm ECAP at 400°C. Employment of this processing route resulted in refining grains by process of dynamic rerystallization and changes in mechanical properties of steel.
Czech name
Využití ECAP metody při zvýšené teplotě pro deformaci uhlíkové ocele
Czech description
V práci je pojednávané o možnosti zjemnění uhlíkové ocele v kombinaci TM zpracování a intenzívní deformace. V první etapě předběžního zjemnění zrna bylo dosaženo termomechanického zpracování ocele a v druhé etapě zjemnění bylo realizováno kanálovým protlačením v zápustce při zvýšené teplotě s aplikací dvou přechodů. Důsledkem kombinovaného využití deformačních metod se dosáhlo intenzivního přetváření ocele s výsledkem zjemnění feritické struktury. Mechanické fragmentování procesu a dynamická rekrystalizace se v značné míře podílely na zjemnění zrna, které ovlynilo deformační mechanické charakteristiky deformované ocele.