Accumulative roll-bonding of aluminium sheets at room and cryogenic temperatures

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F21%3AN0000023" target="_blank" >RIV/26316919:_____/21:N0000023 - isvavai.cz</a>

  • Alternative codes found

    RIV/00216208:11320/21:10437851 RIV/68407700:21340/21:00352510

  • Result on the web

    <a href="http://www.kovmat.sav.sk/article.php?rr=59&cc=4&ss=209" target="_blank" >http://www.kovmat.sav.sk/article.php?rr=59&cc=4&ss=209</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.4149/km_2021_4_209" target="_blank" >10.4149/km_2021_4_209</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    Accumulative roll-bonding of aluminium sheets at room and cryogenic temperatures

  • Original language description

    2 mm thick pure aluminium sheets (99.99 % Al) were processed by accumulative rollbonding (ARB) at room temperature (RT) and under cryogenic conditions (CC, -196 degrees C). Their microstructure was characterized by means of electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM), mechanical properties were examined by hardness measurements. Nearly equiaxed subgrains with a relatively high dislocation density in their interior were observed after the 1st ARB cycle. The following cycles result in subgrain flattening and reduction of inner dislocation density by recovery. The distribution of misorientations of the grain boundaries in CC and RT samples does not differ significantly; only the CC sample has a little higher fraction of the low-angle grain boundaries (LAGB) with misorientation 2 degrees -5 degrees at the expense of LAGB (5 degrees -15 degrees). The hardness increases vitally only during the first ARB cycle at RT; a slight decrease is even observed starting from the 2nd ARB cycle. During processing at CC, this decrease is shifted to the 4th cycle due to reduced post-dynamic recovery at low temperatures.

  • Czech name

  • Czech description

Classification

  • Type

    J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database

  • CEP classification

  • OECD FORD branch

    20501 - Materials engineering

Result continuities

  • Project

    <a href="/en/project/EF15_003%2F0000485" target="_blank" >EF15_003/0000485: Nanomaterials centre for advanced applications</a><br>

  • Continuities

    I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Others

  • Publication year

    2021

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Name of the periodical

    KOVOVE MATERIALY-METALLIC MATERIALS

  • ISSN

    0023-432X

  • e-ISSN

    1338-4252

  • Volume of the periodical

    59

  • Issue of the periodical within the volume

    4

  • Country of publishing house

    CZ - CZECH REPUBLIC

  • Number of pages

    7

  • Pages from-to

    209-215

  • UT code for WoS article

    000703518600001

  • EID of the result in the Scopus database

    2-s2.0-85115761884