Corrosion behaviour of EUROFER in Pb ? Li at 500°C

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F04%3A%230000151" target="_blank" >RIV/26722445:_____/04:#0000151 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Corrosion behaviour of EUROFER in Pb ? Li at 500°C

Original language description

Corrosion resistance of martensitic steel EUROFER 97 was examined in flowing Pb-17Li melt at the temperature of 500°C for 2500 hours. Concentration profiles of steel components near the steel surface, changes of surface morphology as well as of specimenweight loss were observed.

Czech name

Korozní chování oceli EUROFER v Pb-Li při 500°C

Czech description

Korozní odolnost martensitické oceli EUROFER 97 byla hodnocena po expozici v tavenině Pb-17Li při teplotě 500°C podobu 2500 hod. Interakce oceli se slitinou vede k změně koncentračních prvků oceli, morfologie povrchu a ztrátou hmotnosti vzorků.

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JF - Nuclear energy

OECD FORD branch

—

Project

—

Continuities

Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year

2004

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Journal of Nuclear Materials

ISSN

0022-3115

e-ISSN

—

Volume of the periodical

2004

Issue of the periodical within the volume

329-333

Country of publishing house

NL - THE KINGDOM OF THE NETHERLANDS

Number of pages

4

Pages from-to

1384-1387

UT code for WoS article

—

EID of the result in the Scopus database

—